Nickel Substitute Plating Process – Tin Copper Zinc Alloy Plating Process

TINOL NF-65 High Speed Lead-free White Bronze Barrel Plating Process

– Able to form a bright white deposit which can be the surface of the parts or the base layer of the palladium plating and the gold plating.
– Suitable for barrel plating.
– Lead-free; comply with the OKO-TEK requirement.

TINOL NF-67 Lead-free White Bronze Rack Plating Process

– Able to form a bright white deposit which can be the surface of the parts or the base layer of the palladium plating and the gold plating.
Suitable for rack plating.
– Do not induce any allegic reaction caused by nickel deposit.
– Excellent corrosion and abrasion resistance, good solderability and low friction coefficient.
– Can be an alternative to nickel plating process for decorative and electronics plating.

TINOL NF-69 White Bronze Plating Process

– Able to form a bright silvery white deposit with good anti-corrosion ability.
– Suitable as the base layer of aurum plating.
– The layer hardness is 300-400 HV and the weight is only 0.82-0.85 µg/µm.
– Only require 1.4 min (1.5 ASD) to deposit 1µm.